Exaton 19.9.L
19.9.L is used for MIG/MAG welding, and is suitable for joining stainless steels of the 18Cr/8Ni/ELC and 18Cr/8Ni/Nb types for service temperatures up to 350°C (660 F). 19.9.L can be used at cryogenic temperatures down to 4°K (-269°C).
Typisk trækegenskaber
| Betingelse | As Welded | As Welded |
| Trækstyrke | 440 MPa | 610 MPa |
| Trækstyrke | 290 MPa | 460 MPa |
| Forlængelse | 25 % | 38 % |
Svejseparametre
| Current | Voltage | Tråddiameter | Wire Feed Speed | |
| 40-120 A | 15-19 V | 0.8 mm (0.030 in.) | 4.0-8.0 m/min (157-315 in./min) | |
| 60-220 A | 15-28 V | 1.0 mm (0.040 in.) | 4.0-12.0 m/min (157-472 in./min) | |
| 150-260 A | 24-29 V | 1.2 mm (0.047 in.) | 3.0-10.0 m/min (118-394 in./min) | |
| 230-350 A | 25-30 V | 1.6 mm (1/16 in.) | 3.0-5.0 m/min (118-197 in./min) | |
Klassifikationer
| Wire Electrode |
EN ISO 14343-A : G 19 9 L SFA/AWS A5.9 : ER308L Werkstoffnummer : 1.4316 |
Godkendelser
| Godkendelser |
CE EN 13479 DB 43.039.01 VdTÜV 01339 |
| Godkendelser er baseret på fabriksplacering. Kontakt ESAB for flere oplysninger. |
Tilsats karakteristika
| Legeringstype | Austenitic (with approx. 8 % ferrite) 19% Cr - 9% Ni - Low C |
| Beskyttelsesgas | M12, M13 (EN ISO 14175) |
Svejsemetalsanalyse
| Typical Wire Composition % | ||||||||||||||
| C | Co | Cr | Cu | FN WRC-92 | Mn | Mo | N | Nb | Ni | P | S | Si | Ti | |
| 0.010 % | 0.10 % | 19.8 % | 0.2 % | 6 % | 1.8 % | 0.2 % | 0.05 % | 0.01 % | 10.8 % | 0.020 % | 0.009 % | 0.4 % | 0.003 % | |
| Typical Weld Metal Analysis % | ||||||||||||||
| 0.011 % | 0.05 % | 19.6 % | 0.15 % | 6 % | 1.9 % | 0.3 % | 0.06 % | 0.01 % | 10.1 % | 0.018 % | 0.008 % | 0.3 % | 0.003 % | |